Influence of Tucupi on Enamel Surface Roughness, Microhardness, Ultramorphology and Mass Variation.

Aim: The study evaluated the influence of tucupi on enamel surface roughness, microhardness, ultramorphology, and mass variation. Materials and Methods: Ninety healthy bovine incisors were divided into three experimental groups, according to the acidic challenge adopted, being: G1- tucupi, G2- cola-based soft drink, G3-distilled water. The enamel properties (surface roughness, microhardness, ultramorphology and mass variation) of all specimens were evaluated at times T0 (before any intervention), T10 (10 days after the proposed treatments), T20 (20 days after the proposed treatments) and T30 (30 days after the proposed treatments). After confirming the normality of the data (Shapiro-Wilk test), a two-way ANOVA (α = 5%) was performed, followed by Sidak post-test, with results described as mean and standard deviation. Results: The roughness means increased for all tested groups, with no statistical difference only in G3 for all evaluated times. Microhardness of all groups showed a significant decrease over the time, with the lowest average observed in G1 in T30. Considering enamel mass variation, the lowest average was in G2 at time T3, with no statistical difference only in G3 (distilled water) over the time. Regarding ultramorphology (scanning electron microscopy - SEM), only groups G1 and G2, that were exposed to acidic challenges, showed disorganization of the enamel surface layer. Conclusion: It was possible to conclude that tucupi has low pH and high titratable total acidity, being able to gradually decrease enamel microhardness, increasing surface roughness and causing loss of dental enamel.

Excessive Dental Bleaching with 22% Carbamide Peroxide Combined with Erosive and Abrasive Challenges: New Insights into the Morphology and Surface Properties of Enamel.

This study aimed to evaluate the effects of 22% carbamide peroxide combined with an erosive challenge and simulated brushing on enamel. Bovine incisor teeth were divided into G1, tooth bleaching; G2, tooth bleaching + erosive challenge; and G3, tooth bleaching + erosive challenge + simulated brushing, and evaluated at T0, before any intervention; T1, 14 days after the proposed treatments; and T2, 28 days after the proposed treatments. Tooth bleaching was performed daily for 1 h for 28 days. The microhardness, surface roughness, mass variation, and ultrastructure were analyzed at T0, T1, and T2. Two-way analysis of variance for repeated measures was performed and Tukey's post hoc test (α = 5%) was used. The surface roughness increased in groups G2 and G3 as a function of time, whereas microhardness and mass measurements demonstrated a significant reduction for groups associated with challenges. Ultrastructural evaluation indicated a loss of the aprismatic layer and exposure of the enamel prisms in all groups after 14 days of bleaching, with more pronounced results in G2 and G3 after 28 days. In conclusion, abrasive and erosive challenges potentiated the deleterious effects of tooth whitening on microhardness, ultramorphology, and mass, without affecting the roughness of dental enamel.

Influence of Prolonged Tooth Bleaching on Enamel Mass Variation / Influencia del Blanqueo Dental Prolongado en la Variación de Masa del Esmalte Dental

ABSTRACT: The objective evaluate was the influence of prolonged tooth bleaching with 10 % carbamide peroxide (10CP) on tooth enamel mass variation. Ten healthy bovine incisor teeth were divided (n = 5) into G1 - storage in distilled water and G2 - storage in artificial saliva. The samples were weighed in an electronic analytical balance at the following times: T0 - before application of the bleaching gel, T1 - after 14 days of bleaching (the time recommended by the manufacturer), T2 - after 21 days of bleaching (50 % increase in the time recommended by the manufacturer), and T3 - after 28 days of bleaching (100 % increase in the time recommended by the manufacturer). The data were subjected to ANOVA for related samples (p = 0.05). The highest mean was observed in G2 (0.5982 g) and the lowest mean was observed in G1 (0.3074 g) at T2 and T3, respectively. Significant differences were observed between the groups at all times. Overall, 10CP caused variation in the enamel mass after a 100 % increase in the use time recommended by the manufacturer, with a decrease in mass when distilled water was used as the storage medium and an increase when artificial saliva was used.

RESUMEN: El objetivo fue investigar la influencia del blanqueamiento dental prolongado con peróxido de carbamida al 10 % (10CP) sobre la variación de masa del esmalte dental. Las muestras se dividieron en dos grupos: G1, diez dientes sanos de los incisivos bovinos (n = 5) en agua destilada, y G2, almacenamiento en saliva artificial. Las muestras se midieron en una escala analítica electrónica de precisión en los siguientes tiempos: T0-antes de la aplicación del gel blanqueador, T1-después de 14 días de blanqueo (el tiempo recomendado por el fabricante), T2-después de 21 días de blanqueo (aumento de 50 % en el tiempo recomendado por el fabricante), y T3-después de 28 días de blanqueo (aumento de 100 % en el tiempo recomendado por el fabricante). Los datos se presentaron al ANOVA para las muestras relacionadas (P = 0,5). La media más alta se observó en G2 (0,5982 g) y la media más baja se observó en G1 (0,3074 g) en T2 y T3, respectivamente. Se observaron diferencias significativas entre los grupos en todo momento. En general, la 10 CP causó variación en la masa del esmalte después de un aumento de 100 % en el tiempo de uso recomendado por el fabricante, con una disminución en la masa cuando el agua destilada se utilizó como medio de almacenamiento y aumentó cuando se usó saliva artificial.

Is the ethanol wet-bonding technique a promising one? / ¿Es prometedora la técnica de adhesión húmeda en etanol?

The ethanol wet-bonding technique (EWBT) was introduced in an attempt to overcome the problems caused by high hydrophilicity and/or incomplete penetration of most commercially available adhesive systems. This strategy provides better conditions for the inter-diffusion of hydrophobic dentin monomers. Today, there are many EWBT protocols, which yield bonding interfaces with minimal degradation and longer durability compared with commercial hydrophilic adhesive systems. The aim of this review is to discuss in greater detail the EWBT, focused on the following aspects: dentin saturation, hydrophobic primer preparation, inactivation of metalloproteinases (MMPs), dentin biomimetic remineralization and the clinical perspectives of this technique. The present review on the EWBT provides support for a better understanding of the behavior of dentin when exposed to dehydration and hydrophobic monomer interaction. Moreover, additional studies are suggested to investigate the long-term stability of this type of hybrid layer.

La técnica de la adhesión húmeda en etanol (TAHE) se introdujo en un intento de superar los problemas causados por la alta hidrofilicidad y/o la penetración incompleta de la mayoría de los sistemas adhesivos disponibles comercialmente. Esta estrategia ofrece mejores condiciones para la interdifusión de monómeros dentinarios hidrofóbicos. Hoy en día, hay muchos protocolos TAHE que producen las interfaces de unión con mínima degradación y mayor durabilidad en comparación con los sistemas adhesivos hidrofilicos comerciales. El objetivo de esta revisión es discutir con más detalle la TAHE, explicando los siguientes aspectos relacionados: la saturación de la dentina, la preparación del primer hidrofóbico, la inactivación de las metaloproteinasas (MMP's), remineralización biomimética de la dentina, y las perspectivas clínicas de esta técnica. La presente revisión sobre la TAHE proporciona soporte para una mejor comprensión del comportamiento de la dentina cuando es expuesto a la deshidratación y la interacción con monómero hidrófobo. Además, se sugieren estudios adicionales para investigar la estabilidad a largo plazo de este tipo de camada híbrida.

Influência do tipo de unidade fotoativadora (LED ou QTH) na microinfiltração de restaurações com resinas compostas / Influence of type of cure units (LED or QTH) on microleakage of composite resin restorations

Objetivo: Esse estudo testa a hipótese de que não há influência do tipo de unidade fotoativadora (LED ou QTH) na microinfiltração de restaurações classe II de diferentes resinas compostas, realizadas em dentes bovinos. Materiais e Métodos: 20 incisivos bovinos foram selecionados e cavidades classe II foram confeccionadas nas faces proximais de cada dente, totalizando 40 preparos. Os espécimes foram divididos em dois grupos de 10 dentes cada (grupos L e H). No grupo L, as 10 cavidades mesiais foram restauradas com o sistema Single Bond / Z100 (3M) e as 10 cavidades distais foram restauradas com Single Bond / Definite (Degussa) e foram fotopolimerizadas com o LED (Ultraled - Dabi-Atlante). No grupo H os procedimentos restauradores foram similares aos do grupo L, porém os espécimes foram fotopolimerizados com a fonte de luz convencional (Curing light 2500 - 3M). Os dentes foram, então, armazenados em água (37°C) e submetidos à termoreciclagem (5-55°C, 1 min, 500 ciclos). Posteriormente, foram imersos em fucsina básica por 3h, lavados pelo mesmo tempo e seccionados no sentido mesiodistal. A seção com maior extensão de infiltração correspondente a cada resina (mesial e distal) foi selecioanda por meio de lentes de 10X de aumento, avaliadas por três examinadores e a infiltração determinada por escores de 0 a 3. Resultados: Os preparos restaurados com o sistema SB/Definite mostraram maior grau de infiltração comparado ao SB/Z100 e não houve influência da fonte de luz empregada. Conclusão: As cavidades restauradas com ambos os sistemas não foram afetados pela fonte de luz. As restaurações SB/Z100 mostraram menor infiltração em relação ao SB/Definite

Influence of light intensity and curing cycle on microleakage of Class V composite resin restorations

O objetivo deste estudo foi determinar o efeito da polimerização gradual, mediante a utilização de aparelhos de Quartzo-Tungustênio-Halógena (QTH) e Arco de Plasma de Xenônio (PAC), no selamento marginal de restaurações classe V em resina composta com margens localizadas em dentina. Setenta e cinco incisivos bovinos receberam preparos de cavidades classe V, na raiz, com o intuito de situar as margens cavitárias em dentina. Os dentes foram divididos em cinco grupos de acordo com o método de fotoativação. As cavidades, depois de condicionadas, foram tratadas com o sistema adesivo Single Bond (3M Dental) e restauradas com a resina composta Z100 (3M Dental) pela técnica incremental. A fotoativação foi realizada para cada grupo como descrito a seguir: Grupo I: PAC pelo método de fotoativação constante: 1600mW/cm2 – 3s; Grupo II: PAC pelo método de fotoativação por passos (800mW/cm2 – 2s, subindo automaticamente para 1600mW/cm2 – 4s); Grupo III: QTH pelo método de fotoativação constante: 400 mW/cm2 – 40s; Grupo IV: QTH pelo método de fotoativação em rampa: 100 a 600 mW/cm2 – 15s, permanecendo a 600mW/cm2 por mais 25s; Grupo V: QTH pelo método de fotoativação por pulso: 200 mW/cm2 – 3s, tempo de espera de 3min.e a seguir 600mW/cm2 – 30s. Os dentes foram armazenados em água destilada a 37ºC por 30 dias e então submetidos à ciclagem térmica, por 500 ciclos à 5 ºC e 55 ºC. Os ápices dos dentes foram selados com resina composta e os dentes foram cobertos com duas camadas de esmalte para unha, antes da sua imersão em fucsina básica a 0,5%. Os dentes foram seccionados e os cortes foram escaneados para avaliação da área infiltrada por corante por um programa de computador (Image Tools). Os cortes foram também visualizados com lupa para a determinação do grau de penetração do corante na interface dente-restauração por escores. Diferenças estatisticamente significantes foram observadas entre os grupos quanto ao grau e à área de penetração de corante (p < 0,05). Os grupos I e II apresentaram valores significantemente mais altos de infiltração e penetração do corante que os grupos III, IV e V. Em conclusão, o uso da fonte de PAC, no modo constante e por passos, resultou em valores significantemente maiores de infiltração marginal quando comparados com a intensidade de luz média emitida pelos aparelhos de QTH. Os métodos de fotoativação por pulso, rampa e continuo com a fonte de QTH resultaram num grau similar de microinfiltração.

Influence of light intensity and curing cycle on microleakage of Class V composite resin restorations.

The aim of this study was to determine the effect of a softstart polymerization method from Quartz-Tungsten-Halogen (QTH) and Plasma Arc (PAC) curing units on microleakage of Class V composite resin restorations with dentin cavosurface margins. Seventy-five bovine incisors received standardized class V cavities in all dentin margins. Teeth were divided into 5 equal groups according to the curing cycle. The cavities were incrementally restored with a composite resin (Single Bond/Z-100, 3M). Light curing was applied as follows: Group I: PAC light continuous-cycle curing at 1600 mW/cm² for 3s; Group II: PAC light step-cycle curing (2s at 800 mW/cm² then 4s at 1600 mW/cm²); Group III: QTH light continuous-cycle curing at 400 mW/cm² for 40s; Group IV: QTH light ramp-cycle curing (from 100 to 600 mW/cm² in 15s followed by 25s at 600 mW/cm²); Group V: QTH light pulse-delay curing (200 mW/cm² for 3s followed by 3 min delay then 600 mW/cm² for 30s). Teeth were stored in distilled water at 37ºC for 30 days and then subjected to thermocycling for 500 cycles at 5 and 55ºC. Root apices were sealed and teeth coated with nail varnish before they were immersed in 0.5% fuchsine red dye solution. Teeth were then sectioned and slices were scanned with a computer scanner to determine the area of dye leakage using a computer program (Image Tools). Images of tooth slices were also visually examined under magnification and dye penetration along the tooth/restoration interface was scored. Significant differences in the degree of dye penetration and leakage were detected between groups (p<.05). Groups I and II had significantly higher values of dye penetration and leakage than groups III, IV and V. In conclusion, the use of PAC light curing in a continuous or step cycle modes resulted in increased microleakage of Class V resin composite restorations compared with medium intensity QTH light curing. Pulse, ramp and continuous-cycle curing modes with QTH light resulted in similar degrees of microleakage.

Reparos de resina composta envelhecida por oito meses empregando diferentes tratamentos de superfície - avaliação da resistência adesiva / Composite resin repairs aged for eight months using different surface treatments - bond strength evaluation

Este estudo foi realizado devido à necessidade e importância dos procedimentos de reparo em restaurações de resina composta. Propôs-se a avaliar a influência de diferentes tratamentos de superfície na resistência dos reparos. As superfícies de resina, envelhecidas por oito meses, receberam tratamentos de superfície com ácido fosfórico a 37%, ácido fluorídrico a 10% ou jateamento com partículas de óxido de alumínio, seguido da aplicação de um agente adesivo, de um ativador à base de metacrilato mais adesivo ou de um silano mais adesivo. Os reparos foram realizados com a resina composta Z-100, e submetidos ao teste de cisalhamento em uma máquina de ensaios universal. Os melhores resultados foram conseguidos quando o tratamento promoveu uma maior rugosidade superficial e, ainda, a utilização do agente adesivo, com ou sem silano, mostrou-se mais efetiva que a utilização do ativador de superfície, qualquer que fosse o tratamento inicial utilizado

Odontologia estética: estudo das dimensões e formas dos incisivos superiores / Odontología estética: estudio de las dimensiones y formas de los incisivos superiores / Aesthetic dentistry: study of dimensions and contour of upper incisors

Foram analisados as dimensões e os formatos dos incisivos superiores por meio de compasso de ponta seca, bem como o contorno da face, utilizando tomadas radiográficas em uma amostra de 86 adolescentes com idade entre 12 e 17 anos pertencentes à rede estadual de ensino de Londrina. O objetivo foi traçar o contorno vestibular do incisivo central superior e a forma da face, buscando estabelecer uma relação de similaridade. Para tanto, as seguintes medidas dos dentes foram obtidas: distância mésio-distal cervical, distância mésio-distal incisal e comprometimento da coroa clínica. Os dentes foram esquematizados em uma folha de papel milimitrado e, posteriormente, comparados com as medidas das fotografias da face, de frente e em repouso. Medidas essas determinadas no programa de computador Image Tool da Universidade de Santo Antônio - Instituto de Ciências da Saúde - Texas. Os resultados apontaram para a predominância de dentes anteriores superiores triangulares (74 por cento) e de faces triangulares (65 por cento). Também levaram ao estabelecimento de uma relação de similaridade entre os incisivos centrais (94,1 por cento), entre o incisivo central e o incisivo lateral (74,1 por cento), entre o incisivo central e a forma da face (74,4 por cento), servindo de parâmetro para o exame inicial de um tratamento estético

Avaliação da estabilidade de reparos em resina composta por testes de tração e cisalhamento utilizando diferentes tratamentos de superfície / Stability assessment of composite repairs using different surface treatments through tensile and shear tests

Este estudo teve como objetivo avaliar a estabilidade de reparos em resina composta por meio de aplicação de forças de cisalhamento e de tração. Após a simulação do envelhecimento de corpos-de-prova de resina, por 30 dias, foi realizado procedimento de reparo, utilizando-se diferentes tratamentos de superfície. No momento do reparo, cada grupo recebeu um tratamento específico: ácido fosfórico a 35 por cento, ácido fluorídrico a 10 por cento ou jateamento com partículas de óxido de alumínio de 50µm. Tais tratamentos foram seguidos da aplicação de um agente adesivo associado ou não a um agente silanizador. Para a realização dos reparos, a inserção e a polimerização da resina seguiram a técnica incremental. Os espécimes foram novamente armazenados em água destilada e mantidos em estufa a uma temperatura de 37°C por mais 30 dias. Após esse tempo, os corpos-de-prova reparados foram levados a uma máquina de ensaios universal e testados quanto a resistência ao cisalhamento e à tração. A análise dos resultados permitiu verificar que, para os testes propostos, os tratamentos de superfície se comportaram da mesma forma, e o jateamento com óxido de alumínio e o condicionamento com ácido fluorídrico proporcionaram maior rugosidade superficial e maior resistência. Pode-se observar, ainda, que a utilização do agente silano não conseguiu elevar significantemente a resistência dos reparos quando comparados àqueles grupos em que aplicou-se apenas o adesivo

Infiltraçäo marginal em restauraçöes utilizando diferentes métodos de inserçäo da resina / Marginal leakage in restorations according to different composite insertion methods

O presente estudo se propôs a avaliar a infiltraçäo marginal em restauraçöes realizadas pelas técnicas de incremento único e incremental. Foram confeccionadas 32 cavidades de classe V, com margens em esmalte, dimensöes ocluso-cervicais de 2,0mm, mésio-distais de 2,0mm e profundidade de 1,5mm. As cavidades foram restauradas com o sistema restaurador Single Bond/Z250 (3M do Brasil). Os dentes foram divididos em dois grupos. Os grupos diferiam entre si de acordo com a técnica de inserçäo da resina na cavidade. Os resultados mostraram que a técnica incremental apresentou índice de infiltraçäo estatisticamente menor em relaçäo à técnica de incremento único

Estética: critérios para o envolvimento e substituiçäo de estruturas dentárias por materiais restauradores / Aesthetics: criteria for replacing dental structures for restorative materials

Através de uma revisäo em artigos clínicos de divulgaçäo enfocando casos que envolviam estética, foi constatada, em algumas situaçöes, uma abordagem pouco conservativa em relaçäo às estruturas dentárias e circunvizinhas. Percebeu-se que o envolvimento demasiado ou até näo muito precisamente indicado teve como objetivo principal a obtençäo de um resultado estético mais favorável. É entendido que a estética cada vez mais influencia a vida das pessoas, no entanto, é opiniäo dos autores deste artigo que deve haver sempre equilíbrio ao considerar fatores mecânicos, biológicos e estéticos, com o intuito de delinear qualquer tipo de plano de tratamento

Avaliaçäo da resistência adesiva de porcelana fixada à dentina com três cimentos resinosos de dupla polimerizaçäo / Evaluation of shear bond strength of porcelain fixed to dentin with three different dual resin cements

Avaliou-se a resistência adesiva ao cisalhamento de porcelana aderida à dentina com três cimentos resinosos de dupla polimerizaçäo. Os sistemas utilizados foram o Enforce (Dentsply), Scotchbond Resin Cement/Scotchbond Multi-Uso Plus (3M) e Variolink Professional Set (Vivadent). Trinta molares humanos extraídos tiverama superfície oclusal desgastada até a exposiçäo da dentina. Cilindros de porcelana foram confeccionados, cimentados com os respectivos sistemas e o teste de resina adesiva ao cisalhamento foi realizado. O modo de fratura dos espécimes também foi determinado. Concluiu-se que näo houve diferença estatisticamente significante na resistência adesiva ao cisalhamento entre os sistemas de fixaçäo Enforce e Scotchbond Resin Cement/Scotchbond Multi-Uso Plus, porém, estas foram estatisticamente superiores ao sistema de fixaçäo Variolink Professional Set. O modo de fratura dos corpos-de-prova foi predominantemente misto para os sistemas de fixaçäo Enforce e Scotchbond Resin Cement/Scotchbond Multi-Uso Plus, enquanto o sistenma de fixaçäo Variolink Professional Set apresentou fratura adesiva entre a dentina e o sistema de fixaçäo em todos os espécimes

Associação de materiais para restaurações adesivas / Material association for adhesive restorations

Mesmo com o desenvolvimento tecnológico, as resinas compostas apresentam limitações como a contração de polimerização, a resistência ao desgaste, a não liberação de flúor e a sensibilidade de técnica. Uma estratégia para contornar estes problemas é a associação de materiais, onde tenta-se unir as melhores propriedades de cada um, conferindo à restauração um equilíbrio mecânico e biológico e um prognóstico mais favorável

Avaliaçäo clínica de restauraçöes de resina composta: em dentes posteriores com idades de 6 meses a 7 anos / A clinical analysis of composite resin restorations: in posterior teeth following six months to seven years from the procedure

Restauraçöes de resina composta colocadas em dentes posteriores nas clínicas de graduaçäo de Dentística da Faculdade de Odontologia de Baurú, Universidade de Säo Paulo, foram avaliadas com idades entre 6 meses a 7 anos. Os critérios adotados para classificaçäo das restauraçöes foram satisfatórias, insatisfatórias necessitando de reparo ou insatisfatórias necessitando de substituiçäo. De maneira geral, pode-se observar que a cárie secundária foi o fator que mais levou à indicaçäo para substituiçäo das restauraçöes. A reincidência de cárie foi mais freqüente em cavidades com margens localizadas em dentina ou cemento

Avaliaçäo do ionômero de vidro como material intermediário em restauraçöes de resina composta / Evaluation of the glass ionomer as a intermediary material in composite resin restorations

Foi verificada a influência da interposiçäo do ionômero de vidro Vitrebond (3M) em restauraçöes de resina composta feitas com os sistemas Scotchobond Multi-Uso/Z-100(3M) e Optibond/Herculite XRV (Kerr), por meio de testes de infiltraçäo marginal associadas à aplicaçäo de estresses térmico (ciclagem) e mecânico (carga axial)